Properties and welding interface characterization of new-type Au-Ag-Ge brazing alloy;
新型Au-Ag-Ge钎料的性能及焊接界面特征
The results indicate that the base metal, 60wt%BNi2+40wt%BNi5 brazing alloy and BNi2 brazing alloy is with similar passivation current, but the initial passivation potential is increased in turn, which demonstrates that their corrosion resistance is decreased in the same sequence.
通过电化学方法研究了钎料分别为60%BNi2+40%BNi5(质量分数)和BNi2的316L不锈钢钎焊接头在人造海水中的耐腐蚀性能。
The vacuum brazing process of 5CrMnMo steel and YG8 hard metal were studied by using CuMnNi filler metal.
选用CuMnNi钎料,研究了5CrMnMo钢与YG8硬质合金的真空钎焊工艺。
The filler metals and fluxes suitabled for 2A50 aluminum alloy brazing were selected according to the feature of 2A50 aluminum alloy and the test of spreadability and clearance fillabitity.
针对2A50铝合金的特点,根据铺展性、填缝性试验,对适合其钎焊的钎料与钎剂作了选择,进行了接头强度试验。
Wettability of two kinds of Pd-Ni brazing filler metals on Si_3N_4 ceramic;
两种Pd-Ni基高温钎料在Si_3N_4陶瓷上的润湿性
Wettability of Au-Ag-Si brazing filler metal series with Ni;
Au-Ag-Si系钎料合金与Ni的润湿性
The vacuum brazing of 40Cr steel to hard alloy YG8 with CuMnNi brazing filler metal is investigated.
选用CuMnNi钎料,对40Cr钢与YG8硬质合金进行真空钎焊试验,研究钎焊温度和Ni中间层对钎焊接头性能的影响,并用三点弯曲试验确定最佳工艺参数;通过使用扫描电镜观察显微组织及能谱分析钎料中各元素在母材中的扩散情况,并结合钎料在40Cr钢和YG8硬质合金上铺展的润湿角的比较,探讨了该钎料与母材的结合性能。
Development of solders for aluminum brazing;
铝合金钎焊用钎料的发展动态
Effect of adding Bi element on Sn3.5Ag eutectic alloy solder;
Bi对Sn3.5Ag共晶合金钎料性能的影响
Properties and interface microstructure of new type Ag-Cu-Ge solder;
新型Ag-Cu-Ge钎料的性能及钎焊界面特征
The newly developed PdNi-(16-22)Cr-(7-21)V-Si-B(mass fraction,%)brazing filler could be used for joining SiC.
采用座滴法研究了PdNi-Cr-V合金钎料对SiC陶瓷的润湿性。
A series Al-Si alloys for brazing filler was designed.
设计了系列铝硅基合金钎料,采用超音速气体雾化技术制备了钎料粉末,系统地研究了快凝钎料微观组织和焊接性能,优化出一种具有较高综合性能的钎料合金Al-10Si-5Cu-5Zn-0。
For Pd60-Ni40 brazing filler,mainly Pd-Si and Ni-Si phases were formed as the reaction products with Si_3N_4.
采用座滴法研究了三种钎料Pd-N i、PdN i-(5~14)Cr(wt%,下同)和PdN i-(15~26)Cr在S i3N4陶瓷上的润湿情况。