Zinc coatings were prepared by mechanically deposition method with spherical zinc particle and lamellar zinc particle, respectively.
以球状锌粉和片状锌粉为原始锌粉借助于机械镀工艺制备了无结晶锌防护层,运用光学显微镜(OM)、扫描电子显微镜(SEM)观察了镀层的结构形貌:采用XRD技术分析了镀层的物相组成:采用贴滤纸法进行了镀层的孔隙率测试。
Zinc coatings were prepared by mechanically deposition method with spherical zinc particle and lamellar zinc particle,respectively.
以球状锌粉和片状锌粉为原始锌粉制备了机械镀锌层,采用SEM观察了镀层的结构形貌;采用XRD分析了锌粉颗粒形状对镀层物相组成的影响;采用表面洛氏硬度计分析了锌粉颗粒形状对镀层表面硬度的影响;采用中性盐雾实验和电化学极化方法分析了锌粉颗粒形状对镀层耐腐蚀性能的影响。
Applying orthogonal experiment method,the influence of processes of ball silver powder precursor and ball milling on the properties of final flake silver powder were analyzed.
采用正交试验法,分析了前驱体球状银粉的制备及球磨工艺对最终片状银粉性能的影响。
Two Al-C composites were synthesized through solid state method in different temperature,in which the aluminum spherules with particle size of 3 μm was used as matrix and 3,4,9,10-perylene-tetracarboxylic acid-dianhydride(PTCDA) was chosen as modifier.
选用粒径为3μm的球状铝粉作为锂离子电池负极材料,采用小分子有机材料3,4,9,10-苝四酸酐作为改性剂,通过固相法在不同温度下合成两种Al-C复合材料,利用元素分析、XRD、SEM、粒度分布等手段对材料进行了表征,并通过恒流充放电测试对比了铝球和复合材料的电化学性能。
Modification of Micronsized Aluminum Spherules as Anode Materials for Lithium Ion Batteries
微米级球状铝粉作为锂离子电池负极材料的改性研究
metallized slurry explosive
用铝粉敏化的浆状炸药
Research on the Preparation of Spherical Alumina Powder by Microemulsion
微乳液法制备球形氧化铝粉体的研究
Research of Present Situation of Nanometer Aluminum Powder Influenced by Environmental Factors;
环境因素对纳米铝粉影响研究的现状
Characterization of Rapidly Solidified Al-20Si-0.35RE Powder by High Energy Ball Milling
高能球磨稀土高硅铝合金粉末性能表征
Research on Powder Release Agent for Aluminum Alloy Die Casting;
铝合金压铸用粉状脱模剂的开发与性能研究
SINTERING PROCESS OF ALUMINA CERAMICS WIH PLATE-LIKE ALUMINA SEEDS
加入片状晶种的氧化铝粉体的烧结研究
The History and Present Situation of China s Aluminium Foil Ind ustry;
全球铝轧制工业概览系列综述之十九——中国铝箔工业回眸与现状
Aluminium powder for paint
GB/T2083-1989涂料铝粉
Industrial aluminium powder
GB/T2082-1989工业铝粉
Inflammable aluminium powder
GB/T2085-1989易燃铝粉
Bubble aluminium powder
GB/T2084-1989发气铝粉
Study on Geometry of Dish in Powder BaU Forming Mill.
关于粉体成球机盘体几何形状的研究
Preparation and Luminescence Properties of Spherical Yttrium Aluminum Garnet Phosphor (Y_3Al_5O_(12): Ce);
球形钇铝石榴石（Y_3Al_5O_（12）：Ce）荧光粉的制备及荧光性能研究
Effect of aqueous imidazoline corrosion inhibitor on properties of aluminum powder in ball milling
球磨过程中水性咪唑啉类缓蚀剂对铝粉性能的影响
Effect of Milling Pretreatment to Powders on Microstructure and Physical Properties of Al-Si Alloy Materials
粉末球磨预处理对高硅铝合金材料组织与物理性能的影响
Preparation of Copper Powders Covered with Flake Silver by Extraction-Replacement Plating-Ball Milling
用萃取-置换镀-球磨法一次性制备片状银包铜粉
Heat Balance Analysis of Ceramic Ball Heat Carrier and Biomass Powder
陶瓷球固体热载体与粉状生物质的热平衡分析