Slag powder and water glass with proper additives and loading materials were used to prepare coating which was brushed into two layers′ and the surface drying time,water resistance,alkali resistance and bond strength were tested.
采用矿粉和水玻璃为基料,掺加适量助剂和填料,用两层涂刷的方法制备涂料,并测试了涂料表面干燥时间、耐水性、耐碱性和黏结强度。
In order to solve the problems of latent curing at moderate temperature and alkali resistance,a pasty one-component adhesive was formulated with novel accelerator synthesized and selecting main component with alkali resistance.
从解决潜伏性中温固化和耐碱性问题入手,合成了新型促进剂,并选用具有耐碱化学结构的主体材料成分,配制出性能优良的单组分糊状胶黏剂并研究了其耐碱性、固化工艺、黏度变化和贮存期。
Objective:To isolate and identify the alkalitolerant yeast strains from an industrial sewage farm in Wenquan county of Xinjiang,China.
目的:从新疆温泉县一个碱性工业污水处理池中分离并鉴定耐碱酵母菌。
By studying the alkali erosion mechanism and alkali resistance of glass fibers,the paper comes to conclusions that the corrosion of glass fibers by cement matrix includes the chemical action of hydroxide ions and silica tetrahedrons and the physical action in the static fitigue process,and that glass fibers behave quite differentl.
通过对玻璃纤维碱侵蚀机理和耐碱性的探讨,得出了水泥基对玻璃纤维的腐蚀作用包括氢氧离子和硅氧四面体的化学作用和静态疲劳过程的物理作用及玻璃纤维因成分和结构的不同有很大的差异等结论。
The alkali resistance of coatings films,was excellent.
以该固化剂配制的涂料形成的涂膜耐碱性较好。
The alkali resistance faults of electrodeposition coated aluminum profiles are due to non-uniform temperature in baking furnace and lower temperature of some positions.
通过试验及测试,找出了电泳涂漆型材耐碱性不合格的原因,是由于烘干炉内温度不均匀,某些部位的温度过低造成;介绍了烘干炉的改进措施;确定了适宜的烘干工艺。
The assessment of coating alkali corrosion resistance was done through the measurements of weight loss and flexural strength degradation after 48h and longer exposure time in alkali vapor corrosion at 1000℃.
4ZP)涂层,采用XRD、SEM等分析手段研究了涂层的相组成和微观结构,并通过分别测定涂覆和未涂覆涂层试样在1000℃下受腐蚀后的质量损失和强度变化,对涂层的耐碱腐蚀性能进行了表征。