1.马丁体
1.the hard solid solution of iron and carbon used in making hardened steel tools
1.Unlike that of tempered martensite structure, there is little effect of oxygen content on the fatigue properties of ferrite-pearlite steel.
与调质回火马氏体组织不同，氧含量对铁素体-珠光体组织的疲劳性能没有明显的影响。
2.The final structure obtained from tempering a fully hardened steel is called tempered martensite.
回火完全淬硬钢得到的最终组织结构被称为回火马氏体。
3.Tempering is possible because of the instability of the martensite, the principal constituent of hardened steel.
由于马氏体这一淬硬钢主要成分的不稳定性，使得回火成为可能。
4.Bainite also occurs during thermal treatments at cooling rates too fast for pearlite to form, yet not rapid enough to produce martensite.
贝氏体期间也发生在热处理冷却速度太快珍珠岩形式，还没有足够的迅速产生马氏体。
5.Weld metal is composed mainly of acicular ferrite , granular bainite and a small amount of martensite.
焊缝金属主要有针状铁素体+粒状贝氏体+少量马氏体组成。
6.But this kind of stainless steel internal organization for tempering martensite, with guide magnetic, can be magnet attracted.
但这类不锈钢内部组织为回火马氏体，具有导磁性，可被磁铁吸引。
7.The invention discloses a martensite stainless steel with antibacterial property and an application thereof in the industry of hardware.
抗菌马氏体不锈钢及其在五金行业中的应用。
8.The tempered lath martensite grows up with the tempering temperature increasing, however the tendency of growing is not obvious.
随淬火加热温度的升高，板条马氏体逐渐长大，但长大趋势不明显；
9.The martensite stainless steel with antibacterial property is mainly applied to hardware products.
抗菌马氏体不锈钢主要应用于五金产品。
10.Retained austenite reduction and carbide precipitations in the martensite are anticipated by the tempering process.
减少残余奥氏体和马氏体碳化物的降水预计的回火工艺。