1.The ionic chromizing of steel is done by means of ionitriding furnace.
利用离子氮化炉进行钢的离子渗铬。
2.Influence of different pre-heat treatment on low temperature salt-bath chromizing of T10 steel was studied .
研究了不同的预先热处理对T10钢低温盐浴渗铬的影响。
3.Immediate quenching and tempering process of steel T10 after low temperature salt bath chromizing was studied.
研究了T10钢在低温盐浴渗铬后直接淬火并回火工艺。
4.Influence of rare earth on low temperature salt-bath chromizing on 45 steel was studied.
研究了稀土对45钢低温盐浴渗铬的影响。
5.The wear resistance of hard alloy (YG14) and boronizing layer, boron-chromizing layer for steel 45 was studied.
研究了硬质合金（YG14）和45钢渗硼层、硼铬共渗层的耐磨性。
6.The results showed that a chromized layer with good wear resistance could be gained in steel 45 by low temperature salt bath chromizing .
结果表明，45钢在较低温度盐浴可获得良好的渗铬层及优异的耐磨性。
7.Compared with the chromizing layer, the chromosiliconizing layer on cast iron is more unifomrm and more compact.
与单纯渗铬层相比，铸铁铬硅共渗层的连续性和致密性有所增强。
8.On the tendency of non-chromizing to alkali bricks used for cement kiln
水泥窑用碱性砖趋向无铬化
9.Investigation on Glow-discharge Ionized Nickel-chromizing with Arc Source of Ti Alloy and Its Properties
钛合金表面加弧辉光离子渗镍铬及其性能研究
10.Chromizing and Subsequent Nitriding of Austenitic Stainless Steels
奥氏体不锈钢的铬氮复合渗